Electrospinning synthesis and luminescent properties of Lu2O3:Eu3+ nanofibers
来源期刊：JOURNAL OF RARE EARTHS2010年第S1期
论文作者：张浩 陈金灯 郭海
文章页码：232 - 235
摘 要：One-dimensional Lu2O3:Eu3+ nanofibers were prepared by electrospinning followed by high-temperature calcinations.Thermogravimetric and differential thermal analysis,X-ray powder diffraction,Fourier transform infrared spectroscopy,scanning electron microscopy,photoluminescent spectra and decay curves were used to characterize the samples.Results showed that samples began to crystallize at ～500 oC and crystallized completely around 1000 oC.The average diameter of nanofibers（1000 oC annealed） was about 55 nm and the particle size of Lu2O3:Eu3+ increased with increasing annealing temperature.Under ultraviolet excitation,nanofibers exhibited typical red emission of Eu3+ in Lu2O3.The effect of heat-treatment temperature on luminescent properties of nanofibers was also discussed.
张浩，陈金灯，郭海
Department of Physics,Zhejiang Normal University
摘 要：One-dimensional Lu2O3:Eu3+ nanofibers were prepared by electrospinning followed by high-temperature calcinations.Thermogravimetric and differential thermal analysis,X-ray powder diffraction,Fourier transform infrared spectroscopy,scanning electron microscopy,photoluminescent spectra and decay curves were used to characterize the samples.Results showed that samples began to crystallize at ～500 oC and crystallized completely around 1000 oC.The average diameter of nanofibers（1000 oC annealed） was about 55 nm and the particle size of Lu2O3:Eu3+ increased with increasing annealing temperature.Under ultraviolet excitation,nanofibers exhibited typical red emission of Eu3+ in Lu2O3.The effect of heat-treatment temperature on luminescent properties of nanofibers was also discussed.
关键词：