Aging behaviors of Al-Cu-Li-Zr alloy containing Sc

来源期刊:中国有色金属学报(英文版)2005年第z3期

论文作者:梁文杰 潘青林 朱朝明 何运斌 刘元斐

文章页码:12 - 17

Key words:Al-Li alloy; artificial single-aging treatment; microstructures aging behavior

Abstract: Single aging effects on the microstructures and the room-temperature mechanical properties of Al-3.5Cu-1.5Li-0.22(Sc+Zr) alloy were observed using TEM, tensile test and hardness test at room temperature. The results show that the alloy has the character of aging hardening. The aging temperature and aging time have significant effects on the amount and distribution of the major phase of precipitation and strengthening of the alloy. At both high and low temperatures, the precipitation caused by aging is few and coarse, but at high temperature, the coarse equilibrium phases are visible at grain boundaries, therefore, influencing the composite properties of the alloy. The proper artificial single-aging treatment of the alloy is 160℃, 40h. Under this condition, the alloy obtains homogeneously distributed fine T1 phases, which leads to an optimal mechanical properties, i.e. σb is 483MPa, σ 0.2 is 413MPa, and δ is 8.4% for the alloy. However, extending overaging to 50h at 160℃, the coarse equilibrium phases precipitate at grain boundaries leads to wide precipitates-free zone(PFZ) along the grain boundaries, further results in a decrease in the composite properties of the alloy.

基金信息:the National High-Tech Research and Development Program of China

详情信息展示

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号