Optimization of filler metal during superalloy-stainless steel arc brazing
来源期刊：Rare Metals2007年第S1期
论文作者：FAN Chenglei,LIN Sanbao,YANG Chunli,and SONG Jianling State Kay Laboratory of Advanced Welding Production Technology,Harbin Institute of Technology,Harbin ,China
文章页码：36 - 40
摘 要：According to the specification of superalloy-stainless steel arc brazing and characteristic of the base metal,a best filler metal which has relative lower melting point,nice wettability,good weld forming,and adequate shear strength was researched.The experiment results show that wettability of CuFeMn on the stainless steel is very poor,concomitant with a mass of purple soot during the welding which deteriorates the working condition.CuSiMn has the best wettability on both the superalloy and stainless steel,but there remains a lot of pit and slag on the surface of the weld bead.Copper-based solder has the highest melting point and its wettability and clearance fillability are weaker than CuSi3.Wettability and clearance fillability of the CuSi3 are the best in all the candidate filler metals,and its weld is smoothness and has higher shear strength.For its comprehensive ability,CuSi3 is selected as the final filler metal.
FAN Chenglei,LIN Sanbao,YANG Chunli,and SONG Jianling State Kay Laboratory of Advanced Welding Production Technology,Harbin Institute of Technology,Harbin 150001,China
摘 要：According to the specification of superalloy-stainless steel arc brazing and characteristic of the base metal,a best filler metal which has relative lower melting point,nice wettability,good weld forming,and adequate shear strength was researched.The experiment results show that wettability of CuFeMn on the stainless steel is very poor,concomitant with a mass of purple soot during the welding which deteriorates the working condition.CuSiMn has the best wettability on both the superalloy and stainless steel,but there remains a lot of pit and slag on the surface of the weld bead.Copper-based solder has the highest melting point and its wettability and clearance fillability are weaker than CuSi3.Wettability and clearance fillability of the CuSi3 are the best in all the candidate filler metals,and its weld is smoothness and has higher shear strength.For its comprehensive ability,CuSi3 is selected as the final filler metal.