Interpretation of the Habit Plane of d Precipitates in Superalloy Inconel 718
来源期刊：Acta Metallurgica Sinica2018年第2期
论文作者：Wen-Sheng Xu Xiao-Peng Yang Wen-Zheng Zhang
文章页码：113 - 126
摘 要：A calculation method based on a combination of Dg parallelism rule, good matching site（GMS） analysis, CSL/DSCL（coincidence site lattice/displacement shift complete lattice） and the O-lattice theory has been applied to interpret the observation of the habit plane（HP） of the d precipitates and the linear defects in the HP in an Inconel 718 superalloy. The small scattering in the HP orientation around an ideal rational plane is interpreted by the existence of a mixture of two types of steps with different heights and inclinations. These steps play a significant role to enhance the degree of matching in the HP. They are associated with secondary dislocations, with Burgers vectors of 1/6 （1 1 2）y/1/3（0 0 1）, and with a direction parallel to a near-invariant line along （110）y. The spacing of the secondary dislocations projected on the terrace plane is around 6.3 nm. The calculated dislocation structure is in good agreement with the observation.
Wen-Sheng Xu1，Xiao-Peng Yang2，Wen-Zheng Zhang1
1. Key Laboratory of Advanced Materials (MOE), School of Materials Science and Engineering, Tsinghua University2. Oxford Instruments Beijing Office
摘 要：A calculation method based on a combination of Dg parallelism rule, good matching site（GMS） analysis, CSL/DSCL（coincidence site lattice/displacement shift complete lattice） and the O-lattice theory has been applied to interpret the observation of the habit plane（HP） of the d precipitates and the linear defects in the HP in an Inconel 718 superalloy. The small scattering in the HP orientation around an ideal rational plane is interpreted by the existence of a mixture of two types of steps with different heights and inclinations. These steps play a significant role to enhance the degree of matching in the HP. They are associated with secondary dislocations, with Burgers vectors of 1/6 （1 1 2）y/1/3（0 0 1）, and with a direction parallel to a near-invariant line along （110）y. The spacing of the secondary dislocations projected on the terrace plane is around 6.3 nm. The calculated dislocation structure is in good agreement with the observation.
关键词：