Thermostability of Al-Cu-Mg-Fe-Ni Alloy with Trace Scandium and Zirconium

来源期刊:材料科学与工程学报2000年增刊第1期

论文作者:Yu Kun Li Songrui Li Wenxian

关键词:Al-Cu-Mg-Fe-Ni alloy phase Al3(Sc; Zr) tensile property annealing behavior;

摘    要:Three Al-Cu-Mg-Fe-Ni-Sc-Zr ingot metallurgy alloys with different compositions had been prepared. The hardness variations of cold-rolled alloy plates during annealing process had been measured. The tensile properties at both ambient and elevated temperatures were also measured. The microstructures of alloys were observed by using optical microscope and TEM. It was found that the dispersed Al3(Sc, Zr) particles could pin dislocations, stabilize substructures and impede the movement of boundaries. The ambient and elevated temperature properties of alloy with Al3(Sc, Zr) particles were improved. And the tensile strength of alloy did not improve obviously with rich iron and nicker addition.

详情信息展示

Thermostability of Al-Cu-Mg-Fe-Ni Alloy with Trace Scandium and Zirconium

Yu Kun1,Li Songrui1,Li Wenxian1

(1.Department of Materials Science and Engineering, Central South University of Technology,Changsha 410083, P. R. China)

摘要:Three Al-Cu-Mg-Fe-Ni-Sc-Zr ingot metallurgy alloys with different compositions had been prepared. The hardness variations of cold-rolled alloy plates during annealing process had been measured. The tensile properties at both ambient and elevated temperatures were also measured. The microstructures of alloys were observed by using optical microscope and TEM. It was found that the dispersed Al3(Sc, Zr) particles could pin dislocations, stabilize substructures and impede the movement of boundaries. The ambient and elevated temperature properties of alloy with Al3(Sc, Zr) particles were improved. And the tensile strength of alloy did not improve obviously with rich iron and nicker addition.

关键词:Al-Cu-Mg-Fe-Ni alloy phase Al3(Sc; Zr) tensile property annealing behavior;

【全文内容正在添加中】

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号