Development of carbon composite iron ore micropellets by using the microfines of iron ore and carbon-bearing materials in iron making

来源期刊:International Journal of Minerals Metallurgy and Materials2015年第2期

论文作者:Jagannath Pal Satadal Ghorai Avimanyu Das

文章页码:132 - 140

摘    要:Iron ore microfines and concentrate have very limited uses in sintering processes. They are used in pelletization; however, this process is cost intensive. Furthermore, the microfines of non-coking coal and other carbon-bearing materials, e.g., blast-furnace flue dust(BFD) and coke fines, are not used extensively in the metallurgical industry because of operational difficulties and handling problems. In the present work, to utilize these microfines, coal composite iron oxide micropellets(2–6 mm in size) were produced through an innovative technique in which lime and molasses were used as binding materials in the micropellets. The micropellets were subsequently treated with CO2 or the industrial waste gas to induce the chemical bond formation. The results show that, at a very high carbon level of 22wt%(38wt% coal), the cold crushing strength and abrasion index of the micropellets are 2.5–3 kg/cm2 and 5wt%–9wt%, respectively; these values indicate that the pellets are suitable for cold handling. The developed micropellets have strong potential as a heat source in smelting reduction in iron making and sintering to reduce coke breeze. The micropellets produced with BFD and coke fines(8wt%–12wt%) were used in iron ore sintering and were observed to reduce the coke breeze consumption by 3%–4%. The quality of the produced sinter was at par with that of the conventional blast-furnace sinter.

详情信息展示

Development of carbon composite iron ore micropellets by using the microfines of iron ore and carbon-bearing materials in iron making

Jagannath Pal,Satadal Ghorai,Avimanyu Das

National Metallurgical Laboratory, Council of Scientific and Industrial Research

摘 要:Iron ore microfines and concentrate have very limited uses in sintering processes. They are used in pelletization; however, this process is cost intensive. Furthermore, the microfines of non-coking coal and other carbon-bearing materials, e.g., blast-furnace flue dust(BFD) and coke fines, are not used extensively in the metallurgical industry because of operational difficulties and handling problems. In the present work, to utilize these microfines, coal composite iron oxide micropellets(2–6 mm in size) were produced through an innovative technique in which lime and molasses were used as binding materials in the micropellets. The micropellets were subsequently treated with CO2 or the industrial waste gas to induce the chemical bond formation. The results show that, at a very high carbon level of 22wt%(38wt% coal), the cold crushing strength and abrasion index of the micropellets are 2.5–3 kg/cm2 and 5wt%–9wt%, respectively; these values indicate that the pellets are suitable for cold handling. The developed micropellets have strong potential as a heat source in smelting reduction in iron making and sintering to reduce coke breeze. The micropellets produced with BFD and coke fines(8wt%–12wt%) were used in iron ore sintering and were observed to reduce the coke breeze consumption by 3%–4%. The quality of the produced sinter was at par with that of the conventional blast-furnace sinter.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号